铝合金从高温突然降到低温为淬火，例如钢刀刀刃要在水中淬火，才硬和锋利，而铝材的淬火既有水冷淬火，也有风冷淬火。
Aluminum alloy is quenched when it suddenly drops from high temperature to low temperature. For example, the blade of steel knife should be quenched in water before it is hard and sharp. The quenching of aluminum material includes both water cooling quenching and air cooling quenching.
建筑用6063铝型材即用风冷淬火，把淬火后的铝型材放在时效炉内时效一定时间，铝型材内部结晶重新排列，机械强度明显提高。在金属所有合金中，唯独只有铝合金有时效状态。
6063 aluminum profile for construction is quenched by air cooling. The quenched aluminum profile is aged in the aging furnace for a certain time. The internal crystallization of aluminum profile is rearranged, and the mechanical strength is significantly improved. Among all metal alloys, only aluminum alloy has aging state.
铝合金挤压型材成形井盖钢模具 U型槽模具 天津水处理设备 检查井钢模具 保定公司注册 u型槽模具 流水槽模具 温度为460~500度，一般要求淬火后的温度低于200度。通过高温挤压成型，固溶热处理后(淬火)进行人工时效的状态为T5；通过高温挤压成型过程冷却，然后进行人工时效的状态为T6。
The forming temperature of aluminum alloy extruded profile is 460 ~ 500 degrees. Generally, the temperature after quenching is required to be lower than 200 degrees. Through high-temperature extrusion, the state of artificial aging after solution heat treatment (quenching) is T5; The state of cooling through high-temperature extrusion process and then artificial aging is T6.
Aluminum alloy is quenched when it suddenly drops from high temperature to low temperature. For example, the blade of steel knife should be quenched in water before it is hard and sharp. The quenching of aluminum material includes both water cooling quenching and air cooling quenching.
建筑用6063铝型材即用风冷淬火，把淬火后的铝型材放在时效炉内时效一定时间，铝型材内部结晶重新排列，机械强度明显提高。在金属所有合金中，唯独只有铝合金有时效状态。
6063 aluminum profile for construction is quenched by air cooling. The quenched aluminum profile is aged in the aging furnace for a certain time. The internal crystallization of aluminum profile is rearranged, and the mechanical strength is significantly improved. Among all metal alloys, only aluminum alloy has aging state.
铝合金挤压型材成形井盖钢模具 U型槽模具 天津水处理设备 检查井钢模具 保定公司注册 u型槽模具 流水槽模具 温度为460~500度，一般要求淬火后的温度低于200度。通过高温挤压成型，固溶热处理后(淬火)进行人工时效的状态为T5；通过高温挤压成型过程冷却，然后进行人工时效的状态为T6。
The forming temperature of aluminum alloy extruded profile is 460 ~ 500 degrees. Generally, the temperature after quenching is required to be lower than 200 degrees. Through high-temperature extrusion, the state of artificial aging after solution heat treatment (quenching) is T5; The state of cooling through high-temperature extrusion process and then artificial aging is T6.